Investigating the microstructure and properties of Cobalt base alloy Stellite 6 produced by additive manufacturing process with laser direct metal deposition method.
Investigating the microstructure and properties of Cobalt base alloy Stellite 6 produced by additive manufacturing process with laser direct metal deposition method.
Investigating the microstructure and properties of Cobalt base alloy Stellite 6 produced by additive manufacturing process with laser direct metal deposition method.
نوع: Type: thesis
مقطع: Segment: masters
عنوان: Title: Investigating the microstructure and properties of Cobalt base alloy Stellite 6 produced by additive manufacturing process with laser direct metal deposition method.
ارائه دهنده: Provider: salar Hamzehee
اساتید راهنما: Supervisors: Dr Mohsen Sheikhi, Dr Yoosef Mazaheri rodbali
اساتید مشاور: Advisory Professors: Dr. Mahmoud moradi
اساتید ممتحن یا داور: Examining professors or referees: Dr Meysam Nouri, Dr Abbas Pak
زمان و تاریخ ارائه: Time and date of presentation: 2023/03/05, time:13:30
مکان ارائه: Place of presentation: Amphitheater
چکیده: Abstract: In recent years, the process of additive manufacturing with laser has been highly considered as a new solution for the production and repair of metal parts. Having comprehensive information about the microstructural changes and hardness of different areas of the clad sample by changing the process parameters such as: focal distance and laser head to the substrate, laser power, laser scanning direction, and also having a structure free of defects and cracks in the created layers. It is one of the basic requirements of this process. In this research, using direct laser metal deposition method, Stellite 6 alloy was cladded by fiber laser on DIN 1.2714 hot work-grade steel, and the effect of the position of the focal point of the laser beam relative to the surface of the substrate, the distance of the head from the substrate, and the laser power and scanning direction were investigated. At first, 11 single-layer samples were created with a laser power of 250 watts and a variable focal distance from 4 mm above the surface of the substrate to 4 mm below the surface and the distance of the head from the substrate was 15, 17 and 19 mm. The change of these distances on the microstructure and also the hardness were investigated. . Investigations showed that as the focal distance goes from 4 mm above the substrate to 4 mm inside the substrate, the structure becomes finer and it was seen that the hardness also increases and by changing the distance of the nozzle from the substrate from 19 mm above the substrate towards 15 mm from the substrate, the structure is finer and the average hardness is higher. Then, by examining the samples of the single-cladded layer, 5 five-layer samples with powers of 100, 150, 200, 250 and 300 watts with a focal distance of 2 mm above the surface of the substrate were created in the form of bidirectional scanning (reciprocating). The microstructure and hardness were investigated at different points of the samples and it was seen that with increasing laser power from 100 to 300 watts in each sample, the structure became coarser and the average hardness decreased.Then, 3 other samples of five layers, one of which has a power of 250 and a unidirectional scanning direction and a focal distance of 2 mm above the surface of the substrate were created to check the type of scanning direction on the microstructure and hardness of the samples, and two other samples with the same focal distance. And for one-way and two-way scanning, laser power was reduced from 300 to 100 watts in each layer. The purpose of this case was to investigate the type of scanning direction and the power reduction process in each layer on the type of microstructure and hardness of the samples. Investigations showed that the microstructure of bidirectional scanning is more uniform than unidirectional scanning, but its average hardness is lower than unidirectional scanning. Then, the distance of the dendritic arms of the single-layer samples from the three regions of the beginning, middle, and end and of the 5-layer samples in the first to fifth layers was measured in 25 cases in each region, and the average was reported. The distance between the dendritic arms in single-layer samples varies from 1.3 to 3.3 micrometers and in five-layer samples from 1.1 to 4.7 micrometers. Also, in single-layer samples, changing the focal distance led to a change in the dilution of the reference layer in the approximate range of 10 to 90%. Microstructural examination indicated the occurrence of cracking defects in some dilutions. To understand the cause of this phenomenon, one of the solidification crack prediction criteria that was recently proposed was used. This criterion showed that the crack sensitivity increases sharply in the dilution range of 60-90%, which was consistent with the laboratory results. According to this criterion, a sharp increase in the temperature range sensitive to cracking is the cause of cracking in this dilution range.
به اطلاع متقاضیان دکترای سال تحصیلی 1404-1403 رشته های مهندسی (مکانیک - کامپیوتر - برق - مواد - عمران - صنایع) دانشگاه بوعلی سینا می رساند، فهرست اساتید پذیرنده دانشکده مهندسی...
به اطلاع می رساند یک شرکت دانش بنیان در اصفهان نیازمند خدمات تحقیقاتی دانش آموختگان رشته های مواد و شیمی بوده و استخدام می کند. علاقمندان جهت کسب اطلاعات بیشتر و هماهنگی با شماره 03133879868 در...
به گزارش بسنا، مراسم افتتاحیه این پروژه با حضور محمدعلی زلفیگل وزیر علوم، تحقیقات و فناوری و دکتر علیرضا قاسمیفرزاد استاندار همدان، معاونان وزارتخانههای علوم و مسئولان استانی و ریاست...
دفتر هدایت استعدادهای درخشان دانشگاه بوعلیسینا فهرست اسامی دانشجویان برگزیده آموزشی پژوهشی پانزدهمین همایش سالانه دفتر هدایت استعدادهای درخشان سال ۱۴۰۲ را منتشر کرد. اسامی دانشجویان...
بهراد توتونچی دبیر انجمن علمی دانشجویی مهندسی عمران دانشگاه بوعلی سینا، در جلسه ای با حضور نمایندگان دانشگاه های سراسر کشور، با کسب اکثریت آرا انتخابات، به عنوان دبیر...
در هشتمین نشست از دوره یازدهم هیأت ممیزه دانشگاه بوعلیسینا، آقای دکتر علیرضا حاتمی دارای مدرک دکتری در رشته مهندسی برق با ر أ ی اعضاء از مرتبه...
بدینوسیله انتخاب آقای دکتر آرش فتاح الحسینی را به عنوان پژوهشگر برگزیده دانشگاه در گروه فنی و مهندسی به ایشان و خانواده علمی دانشکده مهندسی تبریک عرض نموده و از خداوند متعال...
بدینوسیله انتخاب دو تن از دانشجویان دانشکده مهندسی مهندس راضیه چهارمحالی در مقطع دکتری رشته مهندسی مواد شاخه خوردگی و مهندسی سطح و مهندس امین نظری در مقطع...
بدینوسیله انتخاب سه عضو هیات علمی دانشکده مهندسی جناب آقایان دکتر جواد بهنامیان ، دکتر حسن علم خواه و دکتر محسن گودرزی در...
براساس اطلاعات پایگاه شاخصهای اساسی علم (ESI)، حضوردکتر محمد حسن مرادی از گروه مهندسی برق دانشکده مهندسی در زمره پژوهشگران پراستناد یک درصد برتر دنیا استمرار پیدا کرد. ...
بدینوسیله انتخاب اعضا محترم هیات علمی سرکار خانم دکتر سموئی (گروه مهندسی صنایع)، جناب آقایان دکتر بابائی (گروه مهندسی عمران)، دکتر حاتمی (گروه مهندسی برق)، دکتر ختن لو (گروه مهندسی...
بدینوسیله انتخاب چهار عضو هیات علمی دانشکده مهندسی جناب آقای دکتر جواد بهنامیان از گروه مهندسی صنایع به عنوان پژوهشگر اول برگزیده، جناب آقای دکتر حسن علم خواه از گروه...
به گزارش بسنا و به نقل از سازمان سنجش، آزمون مرحله نهایی بیست و هشتمین دوره المپیاد علمی دانشجویی کشور با حضور نفرات برگزیده آزمون کارشناسی ارشد (متمرکز) و آزمون غیرمتمرکز المپیاد در دانشگاههای...
به اطلاع دانشجویان محترم می رساند سایت کامپیوتر کارشناسی دانشکده مهندسی به دلیل انجام ثبت نام دانشجویان کارشناسی ورودی 1402 از شنبه 1402/7/22 به مدت یک هفته تعطیل می باشد.
به گزارش بسنا و به نقل از معاونت علمی فناوری ریاست جمهوری، در هشتمین دوره تجلیل از سرآمدان علمی کشور در سال ۱۴۰۲ که با حضور معاون علمی و فناوری و اقتصاد دانشبنیان رئیسجمهور و وزیر علوم...
به اطلاع دانشجویان ورودی جدید تحصیلات تکمیلی (ارشد و دکترا) می رساند، یکشنبه 23 مهر ساعت 11 الی 13 در محل آمفی تئاتر دانشکده مهندسی جلسه معارفه با هیات رییسه دانشکده برگزار می شود. ...
بر اساس اطلاعات جدید نمایه استنادی معتبر scopus ۲۰۲۳، با بررسی مقالات مربوط به ۲۰۲۲، 4 عضو هیات علمی و 1 دانش آموخته دانشکده مهندسی و با بررسی کل مقالات مربوط به سال های مختلف، 1 نفر از اعضای هیات...
نظر به مراتب تعهد، تخصص و تجارب ارزشمند جناب آقای دکتر حسن علم خواه و بنا به پیشنهاد رئیس دانشکده مهندسی، به موجب ابلاغی ایشان با حفظ سمت آموزشی به مدت 2 سال به عنوان...
در حکمی از طرف ریاست دانشگاه آقای دکتر امیرسامان خیرخواه به عنوان مدیر گروه رشته مهندسی صنایع منصوب گردید. در این حکم آمده است : « با احترام و آرزوی توفیق الهی، نظر به مراتب تعهد و تجارب...
در حکمی از طرف ریاست دانشگاه آقای دکتر صالح رازینی به عنوان مدیر گروه رشته مهندسی برق منصوب گردید. در این حکم آمده است : « با احترام و آرزوی توفیق الهی، نظر به مراتب تعهد و تجارب ارزنده...